POLYPROPYLENE P400S

Liên hệ để biết giá

PHYSICAL PROPERTIES UNIT TESTING METHOD P400S TYPE* - - H* MELT FLOW RATE g/10/min ASTM D 138 3.5 DENSITY g/cm3 ASTM D 1505 0.910 TENSILE STRENGTH AT YIELD Kg./cm2 ASTM D 638 380 TENSILE STRENGTH AT BREAK Kg./cm2 ASTM D 638 350 ELONGATION AT BREAK % ASTM D 638 500 IZOD IMPACT STRENGTH AT 23oC…

PHYSICAL PROPERTIES	UNIT	TESTING METHOD	P400S
TYPE*	-	-	H*
MELT FLOW RATE	g/10/min	ASTM D 138	3.5
DENSITY	g/cm3	ASTM D 1505	0.910
TENSILE STRENGTH AT YIELD	Kg./cm2	ASTM D 638	380
TENSILE STRENGTH AT BREAK	Kg./cm2	ASTM D 638	350
ELONGATION AT BREAK	%	ASTM D 638	500
IZOD IMPACT STRENGTH AT 23oC	Kg-cm/cm	ASTM D 256	4
IZOD IMPACT STRENGTH AT 0oC	Kg-cm/cm	ASTM D 256	2.5
ROCKWELL HARDNESS	R scale	ASTM D 785	100
FLEXURAL MODULUS	kg./cm2	ASTM D 790	16,000
VICAT SOFTENING POINT	oC	ASTM D 1525	155
HEAT DEFLECTION TEMPERATURE, AT 4.6kg/cm2	oC	ASTM D 648	110
AT 18.5kg/cm2	oC	ASTM D 648	60
APPLICATION: Stretched tape and monofilament for woven bags, woven sheet, ropes, strap and sheet		CHARACTERISTC: High output, good machanical properties
PROCESSING CONDITION GUIDE: The quality of products depend on the quality of resins, extruder machines, and extrusion processing condition. Important factors that should be concerned in processing conditions are melt temperature, stretching temperature and stretching ratio. Moreover, line speed in production and finished products make the condition adjustable. Recommended processing condition. Melt temperature - Cast Film 200-260 deg.C, - Blow Film 190 - 220 deg.C, Stretching Temperature 100-140deg.C/ Stretching Ratio 5-7